罩式退火温度对高强IF钢组织及性能的影响

为研究不同退火温度下高强IF钢的组织性能及织构的变化规律,采用温箱式电阻炉加热模拟罩式退火工艺,研究了不同退火温度下高强IF钢210P1冷轧板力学性能;对不同退火温度钢板的r90进行了统计并对其进行显微组织观察;采用X射线衍射仪及热场发射扫描电镜对不同退火温度的罩式退火成品板进行了织构分析。结果表明,在高强IF钢210P1冷轧板的罩式退火过程中,提高退火温度将使晶粒明显长大。随着退火温度的升高,屈服强度及抗拉强度下降,伸长率升高,n值略有上升,板材横向r值增加较明显,有利织构{111}取向密度增加,不利织构{100}取向密度降低。     

Ablation behavior of (TiZrHfNbTa)C high-entropy ceramics with the addition of SiC secondary under an oxyacetylene flame

The ablation behavior of high-entropy ceramics (HECs) was investigated in this study using an oxyacetylene flame at 2000 °C. Spark plasma sintering was used to construct a dense HEC (TiZrHfNbTa)C with a 20 vol% of SiC addition (HEC-20SiC). The densification of HEC-20SiC can be improved to a certain extent by adding SiC particles, increasing the hardness of HEC-20SiC to up to 24.6 GPa, and the crack deflection observed through the addition of SiC particles were considered to be the strengthening and toughening mechanisms. After ablation, Hf₆Ta₂O₁₇, Ti_5.1Ta_4.9O₂₀, Nb₂Zr₆O₁₇, TaZr_2.75O₈, and SiO₂ can be detected on an ablated surface and HEC-20SiC possesses the minimum mass ablation rate (?1.9 mg s^?1) and line ablation rate (2.1 μm s^?1) among the comparative ceramics. On the one hand, the SiC phase forms gaseous CO, CO₂, and SiO as well as viscous SiO₂ during ablation and some part of the heat can be dissipated by the evaporation of gaseous CO, CO₂, and SiO; further, pore defects can be healed by viscous SiO₂, thus inhibiting the diffusion of reactive oxygen species. On the other hand, the HEC phase with a lattice-distortion caused by single-phase solid-solution can effectively inhibit the invasion of reactive oxygen species and the outward migration of metal atoms. The invasion rate of reactive oxygen is considered to be the main step during HEC-20SiC ablation, and it is believed that higher principal component HECs can improve ablation performance even further.     

Practical Application of the Probabilistic‐Statistical Model of the Suspension Separation in Hydrocyclones

An effective practical approach that allows not only a significant reduction in the scope of practical experiments in the course of studying suspension separation processes in hydrocyclones, but also makes it possible to assess the intensity of random components of the processes and define the interrelation between such components and hydrodynamics of flows in a hydrocyclone is presented. Within the frames of the developed probabilistic‐statistical model of suspension separation in hydrocyclones on the basis of statistical self‐similarity properties, a relationship was found between determined and random components of the processes. This allowed transitioning from three‐parameter probability density functions for suspension particles in hydrocyclones to two‐parameter functions; thus significantly improving the efficiency of practical application of the developed model.     

Manufacturing and characterization of mechanical,biological and dielectric properties of hydroxyapatite-barium titanate nanocomposite scaffolds

In this research, hydroxyapatite (HA)-based ceramics were produced as suitable ceramic implants for orthopedic applications. To improve the physical, mechanical, electrical and biological properties of pure HA, we developed composite scaffolds of HA-barium titanate (BT) by cold isostatic pressing and sintering. Microstructure, crystal phases, and molecular structure were analyzed by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR), respectively. Bulk density values were measured using the Archimedes method. The effect of different percentages of BT on cell proliferation, viability, and ALP activity of dental pulp stem cells (DPSCs) was assessed by ProstoBlue assay, Live/Dead staining, and p-NPP assay. The obtained results indicate that the HA-BT scaffolds possess higher compressive strength, toughness, density, and hardness compared with pure HA scaffolds. After immersing the scaffold in SBF solution, more deposited apatite appeared on the HA-BT, which results in rougher surface on this scaffold thanpure HA. Electrical properties of HA in the presence of BT are improved. Based on the results of cell culture experiments, composites containing 40, 50 and 60 %wt of BT have excellent biocompatibility, with the best results occurring for the sample with 50 %wt BT.     

The use of bio-diesel based additive as rheology improver and pour point depressant of Nigerian waxy crude

The chemical method has proved to be the most effective mitigating method of wax deposition in petroleum system as it deals with the root cause of wax formation. Most of the commercial chemicals in the industry are very expensive and toxic. This paper aims the use of biodiesel based additives for improving the rheological behavior and pour points of waxy crude from Nigeria field. The biodiesels derived additives gave better performance than the commercial chemical and the seed oils as greatly improvement in rheology and pour point values of the waxy crude were observed     

Reduced texaphyrin: A ratiometric optical sensor for heavy metals in aqueous solution

We report here a water-soluble metal cation sensor system based on the as-prepared or reduced form of an expanded porphyrin, texaphyrin. Upon metal complexation, a change in the redox state of the ligand occurs that is accompanied by a color change from red to green. Although long employed for synthesis in organic media, we have now found that this complexation-driven redox behavior may be used to achieve the naked eye detectable colorimetric sensing of several number of less-common metal ions in aqueous media. Exposure to In(III), Hg(II), Cd(II), Mn(II), Bi(III), Co(II), and Pb(II) cations leads to a colorimetric response within 10 min. This process is selective for Hg(II) under conditions of competitive analysis. Furthermore, among the subset of response-producing cations, In(III) proved unique in giving rise to a ratiometric change in the ligand-based fluorescence features, including an overall increase in intensity. The cation selectivity observed in aqueous media stands in contrast to what is seen in organic solvents, where a wide range of texaphyrin metal complexes may be prepared. The formation of metal cation complexes under the present aqueous conditions was confirmed by reversed phase high-performance liquid chromatography, ultra-violet-visible absorption and fluorescence spectroscopies, and high-resolution mass spectrometry.     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Impact sensitivities of energetic materials: Exploring the limitations of a model based only on structural formulas

Using a comprehensive set of drop weight impact test data (h₅₀) newly compiled from literature for 308 materials, a recent approach to predict impact sensitivities of nitro compounds is generalized to most explosive substances of interest. Compared to previous ones, this procedure is more thoroughly validated and exhibits a good predictive value. Furthermore, it yields new insight into the physical mechanisms involved, explaining for instance the unexpected desensitization of some oxygen-deficient triazoles upon nitration.     

The influence of processing conditions on the mechanical properties of poly(aryl-ether-ketone)/polybenzimidazole blends

Interest in developing high-performance blends for niche applications has grown significantly in efforts to meet ever-increasing harsh environment demands. In this work, four model poly(aryl-ether-ketone)/polybenzimidazole (PAEK/PBI) blends were chosen to study the influence of premixing methods, processing, and matrix polymers, on their mechanical properties. Among the model poly(ether ether ketone) (PEEK) and PBI blends, mechanical properties are greatly enhanced by melt premixing. The molding process mainly affects the matrix crystallinity, which in turn greatly influences fracture toughness of the blend. Poly(ether ketone ketone) (PEKK) and PBI blend exhibits a slightly lower tensile strength and fracture toughness than PEEK/PBI due to the differences in inherent properties of PEEK and PEKK matrices and their interfacial interaction with PBI. The processing−structure–property relationship of PAEK/PBI blends is established to help guide optimal design of high-performance polymer blends for structural applications. © 2020 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48966.     

Effects of anion and cation doping on the thermoelectric properties of n-type PbS

The PbCl_xS_1-x and Pb_1-xBi_xS (x? =?0–0.05) bulks were fabricated with a facile method of hydrothermal synthesis and microwave sintering, and the effect of anionic and cationic donors on the thermoelectric performance of PbS was investigated. Although Cl^? and Bi³⁺ both effectively improved the thermoelectric properties of n-type PbS, more excellent thermoelectric performance was obtained from Cl^? doped samples because of higher electrical property and lower thermal conductivity at higher temperature (T? >?600?K). The thermoelectric figure of merit (ZT) reaches 1.04 for PbCl_0.015S_0.985 at 800?K and increases with temperature increasing without sign of saturation, which is probably the highest value ever reported for single-phase polycrystalline n-type PbS. The results also indicate that the hydrothermal synthesis and microwave sintering can realize anion doping as well as cation doping for n-type PbS at low cost, and PbS should be a robust alternative for PbTe thermoelectric materials.